Systems and methods for forming refractory metal nitride layers using organic amines

ABSTRACT

A method of forming (and apparatus for forming) refractory metal nitride layers (including silicon nitride layers), such as a tantalum nitride barrier layer, on a substrate by using an atomic layer deposition process (a vapor deposition process that includes a plurality of deposition cycles) with a refractory metal precursor compound, an organic amine, and an optional silicon precursor compound.

FIELD OF THE INVENTION

[0001] This invention relates to methods of forming refractory metal nitride layers (including silicon nitride layers) on substrates using a vapor deposition process, particularly a multi-step atomic layer deposition process, with a refractory metal precursor compound, an organic amine, and optionally a silicon precursor compound. The formed refractory metal (silicon) nitride layers are particularly useful as diffusion barriers for polysilicon substrates to reduce diffusion of oxygen, copper, or silicon.

BACKGROUND OF THE INVENTION

[0002] In integrated circuit manufacturing, microelectronic devices such as capacitors are the basic energy storage devices in random access memory devices, such as dynamic random access memory (DRAM) devices, static random access memory (SRAM) devices, and ferroelectric memory (FERAM) devices. Capacitors typically consist of two conductors acting as electrodes, such as parallel metal (e.g., platinum) or polysilicon plates, that are insulated from each other by a layer of dielectric material.

[0003] Historically, silicon dioxide has generally been the dielectric material of choice for capacitors. However, the continuous shrinkage of microelectronic devices over the years has led to dielectric layers approaching only 10 Å in thickness (corresponding to 4 or 5 molecules). To reduce current tunneling through thin dielectric layers, high dielectric metal-containing layers, such as Al₂O₃, TiO₂, ZrO₂ HfO₂, Ta₂O₅, (Ba,Sr)TiO₃ Pb(Zr,Ti)O₃ and SrBi₂Ti₂O₉, have been developed to replace SiO₂ layers. However, these metal-containing layers can provide high leakage paths and channels for oxygen diffusion, especially during annealing. Also, an undesirable interfacial layer of SiO₂ is frequently created by oxidation of polysilicon during the annealing of the dielectric layer.

[0004] One way to address these problems is to deposit a thin, conductive, amorphous, metal nitride barrier layer on the substrate prior to the deposition of the thin resistive metal oxide layer. For example, reactive metal silicon nitride barrier metal layers are used to protect polysilicon from oxygen diffusion prior to applying very thin (i.e., less than 10 Å) barium strontium titanate dielectric films.

[0005] Refractory metal nitrides and refractory metal silicon nitrides, such as titanium nitride (Ti—N), tantalum nitride (Ta—N), tungsten nitride (W—N), molybdenum nitride (Mo—N), titanium silicon nitride (Ti—Si—N), tantalum silicon nitride (Ta—Si—N) and tungsten silicon nitride (W—Si—N), are also useful as conductive barrier layers between silicon substrates and copper interconnects to reduce copper diffusion. This copper diffusion has led to degradation of device reliability, causing semiconductor manufacturers to turn toward other less conductive metals, such as aluminum and tungsten.

[0006] Further improvements in high temperature adhesion and diffusion resistance can be realized when about 4 to about 30 atom % silicon is incorporated to form a more amorphous metal silicon nitride layer. Examples of refractory metal silicon nitrides that are useful as barrier layers include tantalum silicon nitride (Ta—Si—N), titanium silicon nitride (Ti—Si—N), and tungsten silicon nitride (W—Si—N).

[0007] Methods for using physical vapor deposition (PVD) methods, such as reactive sputtering, to form Ta—Si—N barrier layers are known. Hara et al., “Barrier Properties for Oxygen Diffusion in a TaSiN Layer,” Jpn J. Appl.-Phys., 36(7B), L893 (1997) describe noncrystalline, low resistivity Ta—Si—N layers that acts as a barrier to oxygen diffusion during high temperature annealing at 650° C. in the presence of O₂. The Ta—Si—N layers are formed by using radio-frequency reactive sputtering with pure Ta and Si targets on a 100 nm thick polysilicon layer. Layers having relatively low silicon content, such as Ta₅₀Si₁₆N₃₄, are stated to have a desirable combination of good diffusion barrier resistance along with low sheet resistance. These Ta—Si—N barrier layers have improved peel resistance over Ta—N barrier layers during annealing conditions.

[0008] Lee et al., “Structural and chemical stability of Ta—Si—N thin film between Si and Cu,” Thin Solid Films, 320:141-146 (1998) describe amorphous, ultra-thin (i.e., less than 100 Å) tantalum-silicon-nitrogen barrier films between silicon and copper interconnection materials used in integrated circuits. These barrier films suppress the diffusion of copper into silicon, thus improving device reliability. Barrier films having compositions ranging from Ta₄₃Si₀₄N₅₃ to Ta_(0.60)Si_(0.11)N_(0.29) were deposited on silicon by reactive sputtering from Ta and Si targets in an Ar/N₂ discharge, followed by sputter-depositing copper films.

[0009] However, when PVD methods are used, the stoichiometric composition of the formed metal nitride and metal silicon nitride barrier layers such as Ta—N and Ta—Si—N can be non-uniform across the substrate surface due to different sputter yields of Ta, Si, and N. Due to the resulting poor layer conformality, defects such as pinholes often occur in such layers creating pathways to diffusion. As a result, the effectiveness of a physically deposited diffusion barrier layer is dependent on the layer being sufficiently thick.

[0010] Vapor deposition processes such as atomic layer deposition (ALD) processes are preferable to PVD processes in order to achieve the most efficient and uniform barrier layer coverage of substrate surfaces. There remains a need for an ALD process to form refractory metal nitrides (especially Ta-N layers) on substrates, such as semiconductor substrates or substrate assemblies.

SUMMARY OF THE INVENTION

[0011] This invention is directed to methods of using vapor deposition processes to deposit refractory metal (silicon) nitride layers (i.e., refractory metal nitride or refractory metal silicon nitride layers) on substrates. The process involves combining one or more refractory metal precursor compounds, one or more nitrogen precursor compounds (organic amines), and optionally one or more silicon precursor compounds.

[0012] In one embodiment, the present invention provides a method of forming a layer on a substrate (preferably in a process for manufacturing a semiconductor structure). The method includes: providing a substrate (preferably, a semiconductor substrate or substrate assembly); providing a vapor that includes one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; providing a vapor that includes one or more organic amines; and directing the vapors including the one or more refractory metal precursor compounds and the one or more organic amines to the substrate to form a refractory metal nitride layer (which preferably forms a diffusion barrier layer) on a surface of the substrate using an atomic layer deposition process (a vapor deposition process that includes a plurality of deposition cycles.

[0013] In another embodiment, the present invention provides a method of forming a layer on a substrate (preferably, in a process for manufacturing a semiconductor structure). The method includes: providing a substrate (preferably, a semiconductor substrate or substrate assembly) within a deposition chamber; providing a vapor that includes one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; directing the vapor that includes the one or more precursor compounds of Formula I to the semiconductor substrate or substrate assembly and allowing the one or more compounds to chemisorb to one or more surfaces of the substrate; providing a vapor that includes one or more organic amines; and directing the vapor that includes the one or more organic amines to the substrate with the chemisorbed compounds thereon to form a refractory metal nitride layer on one or more surfaces of the substrate.

[0014] Preferably, one or more inert carrier gases are introduced into the chamber after the vapor including one or more compounds of Formula I, after the vapor including one or more organic amines, or after both the vaporized precursor compounds of Formula I and the organic amines.

[0015] Optionally, the methods of the present invention can also include providing a vapor that includes one or more metal-containing precursor compounds other than the compounds of Formula I and directing this vapor to the substrate to allow these compounds to chemisorb to one or more surfaces of the substrate. Using such additional precursor compounds, mixed-metal layers can be formed.

[0016] All the metal-containing precursor compounds can be directed to the substrate together (e.g., substantially simultaneously) or separately. They can be directed to the substrate in the same cycle or in separate (e.g., alternating) cycles. They can all be directed to the substrate prior to directing the one or more organic amines to the substrate.

[0017] In a preferred embodiment, method of the present invention include: providing a vapor that includes one or more precursor compounds of Formula I and directing this vapor to the substrate and allowing the one or more compounds to chemisorb to one or more surfaces of the substrate; providing a vapor that includes one or more organic amines and directing this vapor to the substrate with the chemisorbed compounds thereon; providing a vapor that includes one or more precursor compounds other than those of Formula I and directing this vapor to the substrate and allowing the one or more compounds to chemisorb to one or more surfaces of the substrate; and providing a vapor that includes one or more organic amines and directing this vapor to the substrate with the chemisorbed compounds thereon to form a refractory metal nitride layer on one or more surfaces of the substrate. Preferably, the methods include purging excess vapor including one or more precursor compounds from the deposition chamber after chemisorption of the compounds onto the substrate. These steps typically form a cycle that is repeated at least once, and often hundreds of times.

[0018] In another embodiment, the present invention provides a method of manufacturing a memory device structure. The method includes: providing a substrate that includes a silicon-containing surface; providing a vapor that includes one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; directing the vapor that includes the one or more precursor compounds of Formula I to the substrate and allowing the one or more compounds to chemisorb on the silicon-containing surface; providing a vapor that includes one or more organic amines; and directing the vapor that includes the one or more organic amines to the substrate with the chemisorbed compounds thereon to form a refractory metal nitride barrier layer on the silicon-containing surface; providing a first electrode on the barrier layer; providing a high dielectric material over at least a portion of the first electrode; and providing a second electrode over the high dielectric material.

[0019] In yet another embodiment, the present invention provides an atomic layer vapor deposition apparatus that includes: a deposition chamber having a substrate positioned therein; one or more vessels including one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; and one or more vessels including one or more organic amines. Optionally, the apparatus can include one or more vessels with one or more silicon precursor compounds therein and/or one or more reaction gases other than the organic amines and silicon precursor compounds therein.

[0020] “Substrate” as used herein refers to any base material or construction upon which a metal-containing layer can be deposited. The term “substrate” is meant to include semiconductor substrates and also include non-semiconductor substrates such as films, molded articles, fibers, wires, glass, ceramics, machined metal parts, etc.

[0021] “Semiconductor substrate” or “substrate assembly” as used herein refers to a semiconductor substrate such as a metal electrode, base semiconductor layer or a semiconductor substrate having one or more layers, structures, or regions formed thereon. A base semiconductor layer is typically the lowest layer of silicon material on a wafer or a silicon layer deposited on another material, such as silicon on sapphire. When reference is made to a substrate assembly, various process steps may have been previously used to form or define regions, junctions, various structures or features, and openings such as capacitor plates or barriers for capacitors.

[0022] “Layer” as used herein refers to any metal-containing layer that can be formed on a substrate from the precursor compounds of this invention using a vapor deposition process. The term “layer” is meant to include layers specific to the semiconductor industry, such as “barrier layer,” “dielectric layer,” and “conductive layer.” (The term “layer” is synonymous with the term “film” frequently used in the semiconductor industry.) The term “layer” is also meant to include layers found in technology outside of semiconductor technology, such as coatings on glass.

[0023] “Barrier layer” as used herein refers to a conductive, interfacial layer that can reduce diffusion of ambient oxygen through a dielectric layer into a semiconductor substrate (typically a polysilicon substrate) or can reduce diffusion of one layer into another, such as a copper conductive layer into a semiconductor substrate (typically a polysilicon substrate). For this invention, the barrier layer is a tantalum nitride or tantalum silicon nitride layer.

[0024] “Refractory metal” as defined by Webster's New Universal Unabridged Dictionary (1992) is a metal that is difficult to fuse, reduce, or work. For the purposes of this invention, the term “refractory metal” is meant to include the Group IVB metals (i.e., titanium (Ti), zirconium (Zr), hafnium (Hf)); the Group VB metals (i.e., vanadium (V), niobium (Nb), tantalum (Ta)); and the Group VIB metals (i.e., chromium (Cr), molybdenum (Mo) and tungsten (W)).

[0025] “Precursor compound” as used herein refers to refractory metal precursor compounds, nitrogen precursor compounds, silicon precursor compounds, and other metal-containing precursor compounds, for example. A suitable precursor compound is one that is capable of forming, either alone or with other precursor compounds, a refractory metal-containing layer on a substrate using a vapor deposition process. The resulting refractory metal-containing layers also typically include nitrogen and optionally silicon. Such layers are often useful as diffusion barrier layers (i.e., barrier layers).

[0026] “Deposition process” and “vapor deposition process” as used herein refer to a process in which a metal-containing layer is formed on one or more surfaces of a substrate (e.g., a doped polysilicon wafer) from vaporized precursor compound(s). Specifically, one or more metal precursor compounds are vaporized and directed to one or more surfaces of a heated substrate (e.g., semiconductor substrate or substrate assembly) placed in a deposition chamber. These precursor compounds form (e.g., by reacting or decomposing) a non-volatile, thin, uniform, metal-containing layer on the surface(s) of the substrate.

[0027] “Chemical vapor deposition” (CVD) as used herein refers to a vapor deposition process wherein the desired layer is deposited on the substrate from vaporized metal precursor compounds and any reaction gases used within a deposition chamber with no effort made to separate the reaction components. In contrast to a “simple” CVD process that involves the substantial simultaneous use of the precursor compounds and any reaction gases, “pulsed” CVD alternately pulses these materials into the deposition chamber, but does not rigorously avoid intermixing of the precursor and reaction gas streams, as is typically done in atomic layer deposition or ALD (discussed in greater detail below). Also, for pulsed CVD, the deposition thickness is dependent on the exposure time, as opposed to ALD, which is self-limiting (discussed in greater detail below).

[0028] “Atomic layer deposition” (ALD) as used herein refers to a vapor deposition process in which numerous consecutive deposition cycles are conducted in a deposition chamber. Typically, during each cycle the metal precursor is chemisorbed to the substrate surface; excess precursor is purged out; a subsequent precursor and/or reaction gas is introduced to react with the chemisorbed layer; and excess reaction gas (if used) and by-products are removed. As compared to the one cycle chemical vapor deposition (CVD) process, the longer duration multi-cycle ALD process allows for improved control of layer thickness by self-limiting layer growth and minimizing detrimental gas phase reactions by separation of the reaction components. The term “atomic layer deposition” as used herein is also meant to include the related terms “atomic layer epitaxy” (ALE) (see U.S. Pat. No. 5,256,244 (Ackerman)), molecular beam epitaxy (MBE), gas source MBE, organometallic MBE, and chemical beam epitaxy when performed with alternating pulses of precursor compound(s), reaction gas and purge (i.e., inert carrier) gas.

[0029] “Chemisorption” as used herein refers to the chemical adsorption of vaporized reactive precursor compounds on the surface of a substrate. The adsorbed species are irreversibly bound to the substrate surface as a result of relatively strong binding forces characterized by high adsorption energies (>30 kcal/mol), comparable in strength to ordinary chemical bonds. The chemisorbed compounds are limited to the formation of a monolayer on the substrate surface. (See “The Condensed Chemical Dictionary”, 10th edition, revised by G. G. Hawley, published by Van Nostrand Reinhold Co., New York, 225 (1981)). The technique of ALD is based on the principle of the formation of a saturated monolayer of reactive precursor molecules by chemisorption. In ALD one or more appropriate reactive precursor compounds are alternately introduced (e.g., pulsed) into a deposition chamber and chemisorbed onto the surfaces of a substrate. Each sequential introduction of a reactive precursor compound is typically separated by an inert carrier gas purge. Each precursor compound co-reaction adds a new atomic layer to previously deposited layers to form a cumulative solid layer. The cycle is repeated, typically for several hundred times, to gradually form the desired layer thickness. It should be understood, however, that ALD can use one precursor compound and one reaction gas.

BRIEF DESCRIPTION OF THE DRAWINGS

[0030]FIG. 1 shows a device structure including a refractory metal nitride diffusion barrier layer according to the present invention.

[0031]FIG. 2 is a structure showing a high dielectric capacitor including an electrode having a refractory metal nitride diffusion barrier layer according to the present invention.

[0032]FIG. 3 is a perspective view of a vapor deposition coating system suitable for use in the method of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION

[0033] The present invention provides methods of forming a metal-containing layer on a substrate using a vapor deposition process with one or more refractory metal precursor compounds, one or more nitrogen precursor compounds (organic amines), and optionally one or more silicon precursor compounds. For the present invention, the metal-containing layer is a refractory metal nitride layer, preferably, a refractory metal silicon nitride layer. More preferably, the layer is a tantalum silicon nitride barrier layer.

[0034] The layers or films formed can be in the form of refractory metal nitride-containing films or refractory metal silicon nitride-containing films, wherein the layer includes one or more refractory metal nitrides or refractory metal silicon nitrides optionally doped with other metals. Thus, the term “refractory metal (silicon) nitride” films or layers encompass refractory metal nitrides, refractory metal silicon nitrides (of all possible proportions of refractory metal, Si, and N), as well as doped films or layers thereof (e.g., mixed metal (silicon) nitrides). Such mixed metal species can be formed using one or more metal-containing precursor compounds of a formula different from Formula I, which can be readily determined by one of skill in the art.

[0035] The layers of the present invention are preferably conductive. That is, they preferably display an electrical resistivity of no more than about 10 mΩ-cm. The layers of the present invention are typically useful as barrier layers, particularly in the manufacture of semiconductor interconnects. For example, tantalum silicon nitride is being considered as a copper barrier, and is of great interest as a barrier between high dielectric constant oxides and silicon. The addition of silicon to tantalum nitride yields a material that is resistant to crystallization and therefore to diffusion of silicon and metal species via grain boundaries.

[0036] The substrate on which the metal-containing layer is formed is preferably a semiconductor substrate or substrate assembly. Any suitable semiconductor material is contemplated, such as for example, conductively doped polysilicon (for this invention simply referred to as “silicon”). A substrate assembly may also contain a layer that includes platinum, iridium, rhodium, ruthenium, ruthenium oxide, titanium nitride, silicon dioxide, aluminum, gallium arsenide, glass, etc., and other existing or to-be-developed materials used in semiconductor constructions, such as dynamic random access memory (DRAM) devices and static random access memory (SRAM) devices, for example. Preferred substrates include a silicon-containing surface.

[0037] Substrates other than semiconductor substrates or substrate assemblies can be used in methods of the present invention. These include, for example, fibers, wires, etc. If the substrate is a semiconductor substrate or substrate assembly, the layers can be formed directly on the lowest semiconductor surface of the substrate, or they can be formed on any of a variety of the layers (i.e., surfaces) as in a patterned wafer, for example.

[0038] Refractory metal precursor compounds useful in the practice of this invention are of the formula MY_(n) (Formula I) wherein M is a refractory metal, and each Y group is independently a halogen atom or an organic group. Preferably, each Y is independently selected from the group consisting of halogen atoms, alkoxy groups (preferably, (C1-C6)alkoxy groups), and dialkylamino groups (preferably, di(C1-C6)alkylamino groups). More preferably, each Y is a halogen, and most preferably, each Y is a fluorine atom. Preferably, M is a Group IVB (Ti, Zr, Hf), VB (V, Nb, Ta), or VIB (Cr, Mo, W) metal (also referred to as Groups 4, 5, and 6 of the Periodic Table). More preferably, M is Ti, Nb, Ta, Mo, or W. Most preferably, M is Ti or Ta. In Formula I, n is an integer selected to match the valence of the metal M. For example, when M is tantalum (or another pentavalent metal), n is 5.

[0039] Preferably M is tantalum and n is 5 so that the refractory metal precursor compound is a tantalum precursor compound of the formula TaY₅ wherein Y is defined as above. Useful tantalum precursor compounds include TaF₅, TaCl₅, TaBr₅, Ta(OCH₃)₅, Ta(OC₂H₅)₅, Ta(OC₄H₉)₅, pentakis(dimethylamino)tantalum, tris(diethylamino)(ethylimino)tantalum, and tris(diethylamino)(tert-butylimino)tantalum (all available from Sigma-Aldrich Chemical Company, Milwaukee, Wis.). More preferably, the tantalum precursor compound is TaF₅.

[0040] Nitrogen precursor compounds useful in the practice of this invention are organic amines. Preferably, the organic amines are of the formula NR₃ wherein each R is independently hydrogen or an organic group. More preferably, each R is independently hydrogen or an organic group optionally containing silicon atoms, fluorine atoms, or combinations thereof. Preferably, the organic groups include up to six carbon atoms, and more preferably up to four carbon atoms for the organic amine compounds. Thus, particularly preferred embodiments include organic amines in which each R is hydrogen or a (C1-C6) organic group optionally containing silicon and/or fluorine atoms. Examples include tert-butyl amine, diethyl amine, isopropyl amine, hexamethyldisilazane, and tetramethyl disilazane.

[0041] Preferably, the organic amine is a silylated amine, particularly one of the formula H_(x)N(SiR¹ ₃)_(y) wherein y=1-3, x=3-y, and each R¹ is independently hydrogen or an organic group. The term “independently” means that each group may be the same or different. Preferably, the organic groups include up to six carbon atoms, and more preferably up to two carbon atoms for the organic silylated amine compounds. Particularly preferred embodiments include organic silylated amines in which each R¹ is hydrogen or a (C1-C6) organic moiety.

[0042] These nitrogen sources are significant relative to ammonia because they provide conductive metal nitride films with tantalum precursors, whereas ammonia does not. Further, processes using ammonia often lead to solid by-products that can result in detrimental particulates on the substrate or deposits on chamber walls or downstream piping.

[0043] Optional silicon precursor compounds useful in the practice of this invention include silane (SiH₄), disilane (Si₂H₆), halogenated silanes (preferably chlorinated silanes of the formula SiH_(r)Cl₅ wherein r=1-4 and s=4-r), and organic silanes of the formula SiH_(p)R² _(q) wherein p=1-4, q=4-p, and each R² is independently an organic group (preferably having up to six carbon atoms, more preferably up to two carbon atoms, and most preferably, being an organic moiety). Examples include silane (SiH₄), disilane (Si₂H₆), dichlorosilane (SiH₂Cl₂), trichlorosilane (SiHCl₃), and trimethylsilane (SiH(CH₃)₃).

[0044] As used herein, the term “organic group” is used for the purpose of this invention to mean a hydrocarbon group that is classified as an aliphatic group, cyclic group, or combination of aliphatic and cyclic groups (e.g., alkaryl and aralkyl groups). In the context of the present invention, suitable organic groups for precursor compounds of this invention are those that do not interfere with the formation of a metal-containing layer using vapor deposition techniques. In the context of the present invention, the term “aliphatic group” means a saturated or unsaturated linear or branched hydrocarbon group. This term is used to encompass alkyl, alkenyl, and alkynyl groups, for example. The term “alkyl group” means a saturated linear or branched monovalent hydrocarbon group including, for example, methyl, ethyl, n-propyl, isopropyl, t-butyl, amyl, heptyl, 2-ethylhexyl, dodecyl, octadecyl, and the like. The term “alkenyl group” means an unsaturated, linear or branched monovalent hydrocarbon group with one or more olefinically unsaturated groups (i.e., carbon—carbon double bonds), such as a vinyl group. The term “alkynyl group” means an unsaturated, linear or branched monovalent hydrocarbon group with one or more carbon-carbon triple bonds. The term “cyclic group” means a closed ring hydrocarbon group that is classified as an alicyclic group, aromatic group, or heterocyclic group. The term “alicyclic group” means a cyclic hydrocarbon group having properties resembling those of aliphatic groups. The term “aromatic group” or “aryl group” means a mono- or polynuclear aromatic hydrocarbon group. The term “heterocyclic group” means a closed ring hydrocarbon in which one or more of the atoms in the ring is an element other than carbon (e.g., nitrogen, oxygen, sulfur, etc.).

[0045] As a means of simplifying the discussion and the recitation of certain terminology used throughout this application, the terms “group” and “moiety” are used to differentiate between chemical species that allow for substitution or that may be substituted and those that do not so allow for substitution or may not be so substituted. Thus, when the term “group” is used to describe a chemical substituent, the described chemical material includes the unsubstituted group and that group with nonperoxidic O, N, S, Si, F atoms, for example, in the chain as well as carbonyl groups or other conventional substituents. Where the term “moiety” is used to describe a chemical compound or substituent, only an unsubstituted chemical material is intended to be included. For example, the phrase “alkyl group” is intended to include not only pure open chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, tbutyl, and the like, but also alkyl substituents bearing further substituents known in the art, such as hydroxy, alkoxy, alkylsulfonyl, halogen atoms, cyano, nitro, amino, carboxyl, etc. Thus, “alkyl group” includes ether groups, haloalkyls, nitroalkyls, carboxyalkyls, hydroxyalkyls, sulfoalkyls, etc. On the other hand, the phrase “alkyl moiety” is limited to the inclusion of only pure open chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, t-butyl, and the like.

[0046] The precursor compounds may be liquids or solids at room temperature (preferably, they are liquids at the vaporization temperature). Typically, they are liquids sufficiently volatile to be employed using known vapor deposition techniques. However, as solids they may also be sufficiently volatile that they can be vaporized or sublimed from the solid state using known vapor deposition techniques.

[0047] In the practice of this invention, one or more reaction gases other than the nitrogen and silicon precursor compounds described herein can be used if desired. These include, for example, NH₃, N₂H₄, B₂H₆, PH₃, and combinations thereof. Typically, the reaction gases referred to herein do not include metal-containing compounds.

[0048] The precursor compounds can be vaporized in the presence of an inert carrier gas if desired. Additionally, an inert carrier gas can be used in purging steps, as described below. The inert carrier gas is typically selected from the group consisting of nitrogen, helium, argon, and mixtures thereof. In the context of the present invention, an inert carrier gas is one that is generally unreactive with the complexes described herein and does not interfere with the formation of the desired metal-containing film (i.e., layer).

[0049] The deposition process for this invention is a vapor deposition process. Vapor deposition processes are generally favored in the semiconductor industry due to the process capability to quickly provide highly conformal layers even within deep contacts and other openings. Chemical vapor deposition (CVD) and atomic layer deposition (ALD) are two vapor deposition processes often employed to form thin, continuous, uniform, metal-containing (preferably, barrier) layers onto semiconductor substrates. Using either vapor deposition process, typically one or more precursor compounds are vaporized in a deposition chamber and optionally combined with one or more reaction gases to form a metal-containing layer onto a substrate. It will be readily apparent to one skilled in the art that the vapor deposition process may be enhanced by employing various related techniques such as plasma assistance, photo assistance, laser assistance, as well as other techniques.

[0050] The final layer (preferably, a barrier layer) formed preferably has a thickness in the range of about 10 Å to about 500 Å. More preferably, the thickness of the metal-containing layer is in the range of about 30 Å to about 80 Å.

[0051] Preferably, the vapor deposition process employed in the methods of the present invention is a multi-cycle ALD process. Such a process is advantageous (particularly over a CVD process) in that in provides for optimum control of atomic-level thickness and uniformity to the deposited layer (e.g., barrier layer) and to expose the metal precursor compounds to lower volatilization and reaction temperatures to minimize degradation. Typically, in an ALD process, each reactant is pulsed sequentially onto a suitable substrate, typically at deposition temperatures of about 25° C. to about 400° C. (preferably about 150° C. to about 300° C.), which is generally lower than presently used in CVD processes. Under such conditions the film growth is typically self-limiting (i.e., when the reactive sites on a surface are used up in an ALD process, the deposition generally stops), insuring not only excellent conformality but also good large area uniformity plus simple and accurate thickness control. Due to alternate dosing of the precursor compounds and/or reaction gases, detrimental vapor-phase reactions are inherently eliminated, in contrast to the CVD process that is carried out by continuous coreaction of the precursors and/or reaction gases. (See Vehkamäki et al, “Growth of SrTiO₃ and BaTiO₃ Thin Films by Atomic Layer Deposition,” Electrochemical and Solid-State Letters, 2(10):504-506 (1999)).

[0052] A typical ALD process includes exposing an initial substrate to a first chemical species (e.g., refractory metal precursor compound of the formula MY_(n)) to accomplish chemisorption of the species onto the substrate. Theoretically, the chemisorption forms a monolayer that is uniformly one atom or molecule thick on the entire exposed initial substrate. In other words, a saturated monolayer. Practically, chemisorption might not occur on all portions of the substrate. Nevertheless, such an imperfect monolayer is still a monolayer in the context of the present invention. In many applications, merely a substantially saturated monolayer may be suitable. A substantially saturated monolayer is one that will still yield a deposited layer exhibiting the quality and/or properties desired for such layer.

[0053] The first species is purged from over the substrate and a second chemical species (e.g., a different compound of the formula MY_(n), a metal-containing precursor compound of a formula different than MY_(n), or an organic amine compound) is provided to react with the first monolayer of the first species. The second species is then purged and the steps are repeated with exposure of the second species monolayer to the first species. In some cases, the two monolayers may be of the same species. As an option, the second species can react with the first species, but not chemisorb additional material thereto. That is, the second species can cleave some portion of the chemisorbed first species, altering such monolayer without forming another monolayer thereon. Also, a third species or more may be successively chemisorbed (or reacted) and purged just as described for the first and second species.

[0054] Purging may involve a variety of techniques including, but not limited to, contacting the substrate and/or monolayer with a carrier gas and/or lowering pressure to below the deposition pressure to reduce the concentration of a species contacting the substrate and/or chemisorbed compounds. Examples of carrier gases include N₂, Ar, He, etc. Purging may instead include contacting the substrate and/or monolayer with any substance that allows chemisorption by-products to desorb and reduces the concentration of a contacting species preparatory to introducing another species. The contacting species may be reduced to some suitable concentration or partial pressure known to those skilled in the art based on the specifications for the product of a particular deposition process.

[0055] ALD is often described as a self-limiting process, in that a finite number of sites exist on a substrate to which the first species may form chemical bonds. The second species might only bond to the first species and thus may also be self-limiting. Once all of the finite number of sites on a substrate are bonded with a first species, the first species will often not bond to other of the first species already bonded with the substrate. However, process conditions can be varied in ALD to promote such bonding and render ALD not self-limiting. Accordingly, ALD may also encompass a species forming other than one monolayer at a time by stacking of a species, forming a layer more than one atom or molecule thick.

[0056] The described method indicates the “substantial absence” of the second precursor (i.e., second species) during chemisorption of the first precursor since insignificant amounts of the second precursor might be present. According to the knowledge and the preferences of those with ordinary skill in the art, a determination can be made as to the tolerable amount of second precursor and process conditions selected to achieve the substantial absence of the second precursor.

[0057] Thus, during the ALD process, numerous consecutive deposition cycles are conducted in the deposition chamber, each cycle depositing a very thin metal-containing layer (usually less than one monolayer such that the growth rate on average is from about 0.2 to about 3.0 Angstroms per cycle), until a layer of the desired thickness is built up on the substrate of interest. The layer deposition is accomplished by alternately introducing (i.e., by pulsing) refractory metal precursor compound(s) and organic amine compound(s) into the deposition chamber containing a semiconductor substrate, chemisorbing the precursor compound(s) as a monolayer onto the substrate surfaces, and then reacting the chemisorbed precursor compound(s) with the other co-reactive precursor compound(s). The pulse duration of precursor compound(s) and inert carrier gas(es) is sufficient to saturate the substrate surface. Typically, the pulse duration is from about 0.1 to about 5 seconds, preferably from about 0.2 to about 1 second.

[0058] In comparison to the predominantly thermally driven CVD, ALD is predominantly chemically driven. Accordingly, ALD is often conducted at much lower temperatures than CVD. During the ALD process, the substrate temperature is maintained at a temperature sufficiently low to maintain intact bonds between the chemisorbed precursor compound(s) and the underlying substrate surface and to prevent decomposition of the precursor compound(s). The temperature is also sufficiently high to avoid condensation of the precursor compounds(s). Typically the substrate temperature is kept within the range of about 25° C. to about 400° C. (preferably about 150° C. to about 300° C.), which is generally lower than presently used in CVD processes. Thus, the first species or precursor compound is chemisorbed at this temperature. Surface reaction of the second species or precursor compound can occur at substantially the same temperature as chemisorption of the first precursor or, less preferably, at a substantially different temperature. Clearly, some small variation in temperature, as judged by those of ordinary skill, can occur but still be a substantially same temperature by providing a reaction rate statistically the same as would occur at the temperature of the first precursor chemisorption. Chemisorption and subsequent reactions could instead occur at exactly the same temperature.

[0059] For a typical ALD process, the pressure inside the deposition chamber is kept at about 10⁻⁴ torr to about 1 torr, preferably about 10⁻⁴ torr to about 0.1 torr. Typically, the deposition chamber is purged with an inert carrier gas after the vaporized precursor compound(s) have been introduced into the chamber and/or reacted for each cycle. The inert carrier gas(es) can also be introduced with the vaporized precursor compound(s) during each cycle.

[0060] The reactivity of a precursor compound can significantly influence the process parameters in ALD. Under typical CVD process conditions, a highly reactive compound may react in the gas phase generating particulates, depositing prematurely on undesired surfaces, producing poor films, and/or yielding poor step coverage or otherwise yielding non-uniform deposition. For at least such reason, a highly reactive compound might be considered not suitable for CVD. However, some compounds not suitable for CVD are superior ALD precursors. For example, if the first precursor is gas phase reactive with the second precursor, such a combination of compounds might not be suitable for CVD, although they could be used in ALD. In the CVD context, concern might also exist regarding sticking coefficients and surface mobility, as known to those skilled in the art, when using highly gas-phase reactive precursors, however, little or no such concern would exist in the ALD context.

[0061] As stated above, the use of the complexes and methods of forming films of the present invention are beneficial for a wide variety of thin film applications in semiconductor structures. For example, such applications include capacitors such as planar cells, trench cells (e.g., double sidewall trench capacitors), stacked cells (e.g., crown, V-cell, delta cell, multi-fingered, or cylindrical container stacked capacitors), as well as field effect transistor devices.

[0062] Use of the barrier layers of the present invention in semiconductor constructions shall be described generally with reference to FIGS. 1 and 2.

[0063]FIG. 1 illustrates a structure 10 including a substrate assembly 11 and a refractory metal nitride diffusion barrier layer 13 according to the present invention formed on a surface 12 of the substrate assembly 11, e.g., a silicon containing surface. The structure 10 further includes a conductive layer 14 (e.g., a copper layer). The structure 10 is illustrative of the use of a refractory metal nitride diffusion barrier layer for any application requiring an effective barrier layer, for example, to prevent diffusion from a silicon containing surface. In other words, the refractory metal nitride diffusion barrier layer 13 may be used in the fabrication of semiconductor devices wherever it is necessary to prevent the diffusion of one material to an adjacent material. For example, the substrate assembly 11 may be representative of a contact structure having an opening extending to a silicon containing surface. In such a structure, diffusion barriers are commonly used in such openings to prevent undesirable reactions, such as the reaction of a conductive contact material, e.g, copper or aluminum, with the silicon containing surface.

[0064] Further, for example, the refractory metal nitride diffusion barrier layer 13 may be used in the formation of storage cell capacitors for use in semiconductor devices, e.g., memory devices. As further described herein, the refractory metal nitride diffusion barrier layer is used within a stack of layers forming an electrode of a capacitor, e.g., the other layers including layers formed of materials such as platinum, ruthenium oxide, etc. One skilled in the art will recognize that various semiconductor processes and structures for various devices, e.g., CMOS devices, memory devices, etc., would benefit from the barrier characteristics of the barrier layers of the present invention and in no manner is the present invention limited to the illustrative embodiments described herein.

[0065]FIG. 2 shows a structure 50 including substrate assembly 52 (e.g., a silicon substrate) and capacitor structure 54 formed relative thereto. Capacitor structure 54 includes a first electrode 56, a second electrode 60, and a high dielectric constant layer 58 interposed therebetween. For example, the dielectric layer may be any suitable material having a desirable dielectric constant, such as TiO₂, ZrO₂, HfO₂, Ta₂O₅, (Ba,Sr)TiO₃, Pb(Zr,Ti)O₃, or SrBi₂Ti₂O₉. With use of the high dielectric constant layer 58, diffusion barrier properties of the electrodes is particularly important. For example, to function well in a bottom electrode of a capacitor structure, the electrode layer or electrode stack must act as an effective barrier to the diffusion of silicon, particularly due to the processes used to form the high dielectric constant materials. Such diffusion barrier properties are required when the substrate assembly 52 includes a silicon-containing surface 53 upon which the capacitor is formed, e.g., polysilicon, silicon substrate material, N-doped silicon, P-doped silicon, etc., since oxidation of the diffused silicon to form silicon dioxide may result in degraded capacitance, e.g., capacitance for a memory device. In addition, the electrode stack must act as an oxygen barrier (e.g., diffusion barrier layer 62) to protect the silicon-containing surface under the stack from oxidizing. The formation of the refractory metal nitride diffusion barrier layer enhances the barrier properties of the stack.

[0066] A system that can be used to perform an atomic layer deposition of the present invention is shown in FIG. 3. The system includes an enclosed vapor deposition chamber 110, in which a vacuum may be created using turbo pump 112 and backing pump 114. One or more substrates 116 (e.g., semiconductor substrates or substrate assemblies) are positioned in chamber 110. A constant nominal temperature is established for substrate 116, which can vary depending on the process used. Substrate 116 may be heated, for example, by an electrical resistance heater 118 on which substrate 116 is mounted. Other known methods of heating the substrate may also be utilized.

[0067] In this process, precursor compounds 160 (e.g., a refractory metal precursor compound and an organic amine) are stored in vessels 162. The precursor compounds are vaporized and separately fed along lines 164 and 166 to the deposition chamber 110 using, for example, an inert carrier gas 168. A reaction gas 170 may be supplied along line 172 as needed. Also, a purge gas 174, which is often the same as the inert carrier gas 168, may be supplied along line 176 as needed. As shown, a series of valves 180-185 are opened and closed as required.

[0068] The following examples are offered to further illustrate the various specific and preferred embodiments and techniques. It should be understood, however, that many variations and modifications may be made while remaining within the scope of the present invention, so the scope of the invention is not intended to be limited by the examples.

EXAMPLES Example 1 Pulsed CVD of TaN Using TaF₅ and HN(SiHMe₂)₂

[0069] A chamber of configuration shown in FIG. 3 was set up with pneumatic valves under computer control to pulse the valves open in sequential manner. Two reservoirs connected to the chamber contained TaF₅ (Alfa Aesar, Ward Hill, Mass.) and tetramethyldisilazane (TMDS) (Sigma-Aldrich Chemical C., Milwaukee, Wis.). The TaF₅ reservoir was held at 75° C. and the TMDS at ambient. The substrate was a silicon wafer having borophosphosilicate glass (BPSG) as a top layer and was maintained at 255° C. for the deposition.

[0070] Each cycle involved a 2-second pulse of TaF₅ and a 1-second pulse of TMDS, each separated by a 1-second purge with argon and a 2-second pump down under dynamic vacuum. The precursors were introduced without carrier gases, using only a mass flow controller for the TMDS vapor, set at 100 seem. After 300 cycles a TaN film 110 nm thick was obtained, having a resistivity of 7150 μΩ-cm as measured using a four-point probe. The film was nearly 50/50 TaN based on x-ray photoelectron spectroscopy (XPS) analysis, and had <5% oxygen, <2% carbon, and no detected fluorine. X-ray diffraction analysis of the deposited film verified that it was crystalline TaN.

[0071] The complete disclosures of the patents, patent documents, and publications cited herein are incorporated by reference in their entirety as if each were individually incorporated. Various modifications and alterations to this invention will become apparent to those skilled in the art without departing from the scope and spirit of this invention. It should be understood that this invention is not intended to be unduly limited by the illustrative embodiments and examples set forth herein and that such examples and embodiments are presented by way of example only with the scope of the invention intended to be limited only by the claims set forth herein as follows. 

What is claimed is:
 1. A method of manufacturing a semiconductor structure, the method comprising: providing a semiconductor substrate or substrate assembly; providing a vapor comprising one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; providing a vapor comprising one or more organic amines; and directing the vapors comprising the one or more refractory metal precursor compounds and the one or more organic amines to the semiconductor substrate or substrate assembly to form a refractory metal nitride layer on a surface of the semiconductor substrate or substrate assembly using an atomic layer deposition process comprising a plurality of deposition cycles.
 2. The method of claim 1 wherein each Y is independently selected from the group consisting of halogen atoms, alkoxy groups, and dialkylamino groups.
 3. The method of claim 2 wherein each Y is independently a halogen atom.
 4. The method of claim 1 wherein M is tantalum and n is
 5. 5. The method of claim 4 wherein each Y is a fluorine atom.
 6. The method of claim 1 wherein the organic amine is of the formula NR₃ wherein each R is independently hydrogen or an organic group.
 7. The method of claim 6 wherein the organic amine is a silylated amine.
 8. The method of claim 7 wherein the silylated amine is of the formula H_(x)N(SiR¹ ₃)_(y) wherein y=1-3 and x=3-y, and each R¹ is independently hydrogen or an organic group.
 9. The method of claim 1 further comprising providing a vapor comprising one or more silicon precursor compounds and directing the vaporized silicon precursor compounds to the semiconductor substrate or substrate assembly to form a refractory metal silicon nitride layer.
 10. The method of claim 8 wherein the silicon precursor compound is of the formula H_(x)N(SiR¹ ₃)_(y) wherein y=1-3, x=3-y, and each R¹ is independently hydrogen or an organic group.
 11. The method of claim 1 wherein the semiconductor substrate or substrate assembly comprises a silicon-containing surface.
 12. The method of claim 1 wherein the formed layer has a thickness of about 10 Å to about 500 Å.
 13. The method of claim 1 wherein the formed layer is a diffusion barrier layer.
 14. The method of claim 13 further comprising forming an electrode over at least a portion of the barrier layer.
 15. The method of claim 14 further comprising forming a dielectric layer over at least a portion of the electrode.
 16. The method of claim 1 further comprising providing one or more reaction gases other than the organic amines and directing the one or more reaction gases to the semiconductor substrate or substrate assembly.
 17. The method of claim 16 wherein the reaction gas is selected from the group consisting of NH₃, N₂H₄, B₂H₆, PH₃, and combinations thereof.
 18. A method of manufacturing a semiconductor structure, the method comprising: providing a semiconductor substrate or substrate assembly within a deposition chamber; providing a vapor comprising one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; directing the vapor comprising the one or more precursor compounds of Formula I to the semiconductor substrate or substrate assembly and allowing the one or more compounds to chemisorb to one or more surfaces of the semiconductor substrate or substrate assembly; providing a vapor comprising one or more organic amines; and directing the vapor comprising the one or more organic amines to the semiconductor substrate or substrate assembly with the chemisorbed compounds thereon to form a refractory metal nitride layer on one or more surfaces of the semiconductor substrate or substrate assembly.
 19. The method of claim 18 further comprising providing a vapor comprising one or more metal-containing precursor compounds other than the compounds of Formula I and directing the vapor to the semiconductor substrate or substrate assembly to allow the compounds other than the compounds of Formula I to chemisorb to one or more surfaces of the semiconductor substrate or substrate assembly.
 20. The method of claim 19 wherein the vapor comprising one or more compounds of Formula I and the vapor comprising one or more compounds other than those of Formula I are directed to the semiconductor substrate or substrate assembly prior to directing the vapor comprising one or more organic amines to the semiconductor substrate or substrate assembly.
 21. The method of claim 20 wherein the vapor comprising one or more compounds of Formula I and the vapor comprising one or more compounds other than those of Formula I are directed to the semiconductor substrate or substrate assembly substantially simultaneously.
 22. The method of claim 20 comprising: providing a vapor comprising one or more precursor compounds of Formula I and directing this vapor to the substrate and allowing the one or more compounds to chemisorb to one or more surfaces of the semiconductor substrate or substrate assembly; providing a vapor comprising one or more organic amines and directing this vapor to the substrate with the chemisorbed compounds thereon; providing a vapor comprising one or more precursor compounds other than those of Formula I and directing this vapor to the semiconductor substrate or substrate assembly and allowing the one or more compounds to chemisorb to one or more surfaces of the semiconductor substrate or substrate assembly; and providing a vapor comprising one or more organic amines and directing this vapor to the semiconductor substrate or substrate assembly with the chemisorbed compounds thereon to form a refractory metal nitride layer on one or more surfaces of the semiconductor substrate or substrate assembly.
 23. The method of claim 22 further comprising purging excess vapor comprising the one or more precursor compounds from the deposition chamber after chemisorption of the compounds onto the semiconductor substrate or substrate assembly.
 24. The method of claim 23 wherein purging comprises purging with an inert carrier gas.
 25. The method of claim 24 wherein the inert carrier gas is selected from the group consisting of nitrogen, helium, and argon.
 26. The method of claim 18 wherein the providing and directing steps are repeated at least once.
 27. The method of claim 18 wherein the temperature of the semiconductor substrate or substrate assembly is about 25° C. to about 400° C.
 28. The method of claim 18 wherein the deposition chamber pressure is about 10⁻⁴ torr to about 1 torr.
 29. The method of claim 18 wherein each Y is independently selected from the group consisting of halogen atoms, alkoxy groups, and dialkylamino groups.
 30. The method of claim 18 wherein M is tantalum and n is
 5. 31. A method of forming a layer on a substrate, the method comprising: providing a substrate; providing a vapor comprising one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; providing a vapor comprising one or more organic amines; and directing the vapors comprising the one or more refractory metal precursor compounds and the one or more organic amines to the substrate to form a refractory metal nitride layer on a surface of the substrate using an atomic layer deposition process comprising a plurality of deposition cycles.
 32. The method of claim 31 wherein each Y is independently selected from the group consisting of halogen atoms, alkoxy groups, and dialkylamino groups.
 33. The method of claim 31 wherein the organic amine is of the formula NR₃ wherein each R is independently hydrogen or an organic group.
 34. The method of claim 31 wherein the organic amine is a silylated amine.
 35. The method of claim 34 wherein the silylated amine is of the formula H_(x)N(SiR¹ ₃)_(y) wherein y=1-3 and x=3-y, and each R¹ is independently hydrogen or an organic group.
 36. The method of claim 31 further comprising providing a vapor comprising one or more silicon precursor compounds and directing the vaporized silicon precursor compounds to the substrate to form a refractory metal silicon nitride layer.
 37. The method of claim 36 wherein the silicon precursor compound is of the formula H_(x)N(SiR¹ ₃)_(y) wherein y=1-3, x=3-y, and each R¹ is independently hydrogen or an organic group.
 38. The method of claim 36 further comprising providing one or more reaction gases other than the organic amines and silicon precursor compounds and directing the one or more reaction gases to the substrate.
 39. A method of forming a layer on a substrate, the method comprising: providing a substrate within a deposition chamber; providing a vapor comprising one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; directing the vapor comprising the one or more precursor compounds of Formula I to the substrate and allowing the one or more compounds to chemisorb to one or more surfaces of the substrate; providing a vapor comprising one or more organic amines; and directing the vapor comprising the one or more organic amines to the substrate with the chemisorbed compounds thereon to form a refractory metal nitride layer on one or more surfaces of the substrate.
 40. The method of claim 39 further comprising providing a vapor comprising one or more metal-containing precursor compounds other than the compounds of Formula I and directing this vapor to the substrate to allow these compounds to chemisorb to one or more surfaces of the substrate.
 41. The method of claim 40 wherein the vapor comprising one or more compounds of Formula I and the vapor comprising one or more compounds other than those of Formula I are directed to the substrate prior to directing the vapor comprising one or more organic amines to the substrate.
 42. The method of claim 40 wherein the vapor comprising one or more compounds of Formula I and the vapor comprising one or more compounds other than those of Formula I are directed to the substrate substantially simultaneously.
 43. The method of claim 40 comprising: providing a vapor comprising one or more precursor compounds of Formula I and directing this vapor to the substrate and allowing the one or more compounds to chemisorb to one or more surfaces of the substrate; providing a vapor comprising one or more organic amines and directing this vapor to the substrate with the chemisorbed compounds thereon; providing a vapor comprising one or more precursor compounds other than those of Formula I and directing this vapor to the substrate and allowing the one or more compounds to chemisorb to one or more surfaces of the substrate; and providing a vapor comprising one or more organic amines and directing this vapor to the substrate with the chemisorbed compounds thereon to form a refractory metal nitride layer on one or more surfaces of the substrate.
 44. The method of claim 43 further comprising purging excess vapor comprising the one or more precursor compounds from the deposition chamber after chemisorption of the compounds onto the substrate.
 45. The method of claim 43 wherein the providing and directing steps are repeated at least once.
 46. The method of claim 39 wherein the temperature of the semiconductor substrate or substrate assembly is about 25° C. to about 400° C.
 47. The method of claim 39 wherein the deposition chamber pressure is about 10⁻⁴ torr to about 1 torr.
 48. The method of claim 39 wherein each Y is independently selected from the group consisting of halogen atoms, alkoxy groups, and dialkylamino groups.
 49. A method of manufacturing a memory device structure, the method comprising: providing a substrate comprising a silicon-containing surface; providing a vapor comprising one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; directing the vapor comprising the one or more precursor compounds of Formula I to the substrate and allowing the one or more compounds to chemisorb on the silicon-containing surface; providing a vapor comprising one or more organic amines; and directing the vapor comprising the one or more organic amines to the substrate with the chemisorbed compounds thereon to form a refractory metal nitride barrier layer on the silicon-containing surface; providing a first electrode on the barrier layer; providing a high dielectric material over at least a portion of the first electrode; and providing a second electrode over the high dielectric material.
 50. The method of claim 49 further comprising providing a vapor comprising one or more silicon precursor compounds and directing the vapor to the substrate with the chemisorbed compounds thereon to form a refractory metal silicon nitride barrier layer on the silicon-containing surface.
 51. The method of claim 49 wherein each Y is independently a halogen atom.
 52. The method of claim 49 wherein M is tantalum and n is
 5. 53. An atomic layer deposition apparatus comprising: a deposition chamber having a substrate positioned therein; one or more vessels comprising one or more refractory metal precursor compounds of the formula MY_(n) (Formula I), wherein M is a refractory metal, each Y is independently a halogen atom or an organic group, and n is an integer selected to match the valence of the metal M; and one or more vessels comprising one or more organic amines.
 54. The apparatus of claim 53 further comprising one or more vessels comprising one or more silicon precursor compounds.
 55. The apparatus of claim 53 further comprising one or more vessels comprising one or more reaction gases other than the organic amines. 